Fiberthree F3 PA Pure Lite

High-performance polyamide based on PA 12 with a smooth surface

Out of StockOur shop no longer sells this product.

Product information & technical details

Manufacturers: Fiberthree
Diameter: 1,75 mm, 2,85 mm
Product types: PA - Nylon Filaments
Filament colour: White
Net weight: 1000 g, 2000 g
Recommended processing temperature: 260 - 290 °C
Recommended heating temperature: < 90 °C

Description

F3 PA Pure Lite is a technical filament made of polyamide, which has been specially modified for 3D printing.

Material properties

The material shows superior strength while remaining impact resistance with very little tendency to warp and good layer adhesion. Due to the good heat and load resistance, this material is recommended for all high-strength parts. The printed parts show a very attractive surface texture in matt antique white. It is a very stiff filament that can break only with tight flex.

In contrast to F3 PA-CF Lite, this material is unfilled and has a higher heat requirement when melting than F3 PA Pure Pro. However, the moisture sensitivity is also lower than F3 Pa Pure Pro.

It offers itself as a comparative material for the influence of fibres, for a multi-material component and as an alternative if a smooth surface is required or if the fibres are unsuitable.

Processing

Wear-resistant nozzles are strongly recommended for processing the material.

The material must be stored dry in order to achieve reliable printing results under all conditions